| Alloy Name | |||||||||||||||||
| AMW-22 | IS | DIN CEN/TS 13388 | UNS | JIS | KMW | ||||||||||||
| CuZn10 | CuZn10 | CW50IL | C22000 | C2200 | CuZn10 | ||||||||||||
| Chemical Composition | (% By Weight) |
| Cu | 89.0 91.0% |
| Pb | < 0.05 % |
| Fe | < 0.05 % |
| Zn | Reminder % |
| Total Impurity | 0.13% |
| Main Applications | |
| Electrical | Wave guides, Rotor Bar-AC Motors, Cable Warp |
| Consumer | House for Lipstick compacts, Costume Jewelry, Ball point Pens. |
| Fasteners | Screw Shells, Bolts, Line Clamps, Rivets |
| Typical Applications | Jewellery and metal good, Components for the electrical industry, Leadframes. |
| Physical Properties Typical values in annealed temper at 20°C | ||
| Density | 8.80 | g/cm3 |
| Thermal expansion coefficient −191 .. 16 / - 0 .. 300°C | 9.0/18.2 | 10-6/K/10-6/K |
| Specific heat capacity | 0.376 | J/(g.K) |
| Thermal conductivity | 184 | W/(m.k) |
| Electrical conductivity (1 MS/m = 1m/(0 mm2)) | > 25 | MS/M |
| Electrical conductivity (IACS) | 43 | % |
| Thermal coefficient of electrical resistance (0 .. 200 C) | 1.8 | 10-3/K |
| Modulus of elasticity (1GPa = 1 kN/mm2) cold formed | 99.... 115/124 | GPa / Gpa |
| Mechanical Properties (EN 1652) | ||||
| Temper | Tensile Strength Rm MPa (N/mm2) |
Yield Strength Rp0.2 MPa (N/mm2) |
Elongation Minimum A50mm % | Hardness HV |
| O (SOFT) | 245 Min | < 140 | 35 Min | 75 Max |
| HB (Half Hard) | 310 Min | > 200 | 7 Min | 95 Min |
| HD (Hard) | 350 Min | > 290 | 3 Min | 110 Min |
Cold formability
Hot formability
Soldering
Brazing
Oxyacetylene welding
Gas shielded arc welding
Resistance Welding
Machinability
Excellent
Good
Excellent
Excellent
Good
Good
Not Recommended
Not Recommended